Equivalent table
| TOCT 14959 | DIN 17221 | GB/T 1222 | NF A35-571 | ISO 683-14 | ASTM | JIS G4801 | |
| A29M | A322 | ||||||
| 60C2T 60C2A | 60SiCr7
| 60Si2Mn
| 61SiCr7
| 59Si7
| 9260
| G92600
| SU P6 SU P7 |
Applications
60SI2MN steels, Highlight the advantage is good hardenability, another hot working performance, comprehensive mechanical properties,
Decarburization resistance is also good big cross section of various important spring, such as automobile, locomotive, large plate spring, spring, etc. 60SI2MN Spring main used for heavy vehicles, tractors, industrial production load, stress and the diameter of the larger plate spring and helical spring.
Chemical composition
| C | Si | Mn | Cr | p | S | Ni | Cu |
| 0.56-0.64 | 1.50-2.00 | 0.60-0.90 | ≤0.35 | ≤0.035 | ≤0.035 | ≤0.35 | ≤0.25 |
Heat treatment Related
- Annealing of 60SI2MN Spring Steel
Slowly heated to 740-770 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. The 60SI2MN tool steel will get MAX 250 HB （Brinell hardness）.
- Hardening of 60SI2MN Spring Steel
60SI2MN steels should be heated uniformly to 830-860°C (1526-1580°F) until completely heated through. About 30 min per 25 mm of ruling section is to be provided and then the steels should be immediately quenched in oil. Get Hardness 61 Min.
- Tempering of 60SI2MN Spring Steel
Tempering of 60SI2MN steels is performed at 480-530°C, Soak well at the selected temperature and soak for at least one hour per 25mm of total thickness. Hardness values at different temperatures after tempering HRC: 150°C-61HRc,200°C-60HRC,300°C-56HRC,400°C-51HRC,500°C-43HRC,550°C-38HRC,600°C-33HRC,650°C-29HRC.
Propriedades mecânicas
The mechanical properties of 60SI2MN Spring Steels are outlined in the following table.
| Tensile strength | Conditions to yield strength | Elongation | Reduction of area | Hardness (Hot Rolled) | Hardness (Cold Drawn) |
| σb (MPa)：≥1274(130) | σ0.2 (MPa)：≥1176(120) | δ10 (%)：≥5 | ψ (%)：≥25 | ≤321HB; |